301 Stainless Steel

www.decodesk.com
DÉTAILS TECHNIQUES
Acier inoxydable 301
STANDARDS APPLICABLES: ASTM A-240, ASTM A-666, UNS S30100, AMS5517, AMS5518,
AMS 5519
ÉQUIVALENCES: DIN: 1.4310, X12CrNi17-7
JIS: SUS301
C
301
COMPOSITION CHIMIQUE (%)
Si
Cr
Ni
Mn
0.15 max
2.0 max
1.0 max
16.0-18.8
6.0-8.0
Autres
P 0.040 max, S
0.030 max, N
0.10 max
PROPRIÉTÉS PHYSIQUES TYPIQUES
DENSITÉ
8.02 g/cm3
(0.290 lb/plg3)
PROPRIÉTÉS MÉCANIQUES TYPIQUES
TEMPÉRATURE
RESISTANCE À LA
TENSION
LIMITE D’ÉLASTICITÉ
(0.02%)
ALLONGEMENT (2")
(%)
DURETÉ TYPIQUE
75 KSI min
30 KSI min
40 min
92 Rb max
RECUIT
(515 MPa min)
(205 MPa min)
90 KSI min
45 KSI min
41 min
1/16 H
(620 MPa min)
(310 MPa min)
100 KSI min
55 KSI min
40 min
1/8 H
(690 MPa min)
(380 MPa min)
125 KSI min
75 KSI min
25 min
25-30 HRC
1/4 H
(860 MPa min)
(515 MPa min)
150 KSI min
110 KSI min
15% < 0.015" 18%
30-35 HRC
1/2 H
(760 MPa min)
0.015"
(1035 MPa min)
175 KSI min
135 KSI min
10% < 0.015" 12%
35-40 HRC
3/4 H
(1205 MPa min)
(930 MPa min)
0.015"
185 KSI min
140 KSI min
8% < 0.015" 9%
40-45 HRC
TRÈS DUR
(1275 MPa min)
0.015"
(965 MPa min)
270 KSI min
EXTRA DUR
(1860 MPa min)
185 KSI min
RESSORTS
40-45 HRC
(1275 MPa min)
NOTE: La dureté est purement indicative, RT et RC sont les seules propriétés obligatoires.
CARACTÉRISTIQUES
L’acier inoxydable type 301 est un acier inoxydable austénitique capable d’une haute résistance mécanique et d’une ductilité au travers du
travail en froid; cet acier ne peut pas s’endurcir par traitement thermique et est non-magnétique en condition “recuit” (annealed). Il
commence à se magnétiser après un travail en froid. Le type 301 est préférable aux types 302 et 304 en conditions endurcies car il atteint
un haut niveau d’allongement et une haute résistance, ce qui facilite sa fabrication et une large gamme d’utilisation.